Quote:
Originally Posted by Eman
When you say welded what are you welding the steel pickup to cast iron with?
|
Good morning Eman and to all,
I've been brazing them. In the past we've tried MiG welding and TiG welding and had problems with the castings cracking during cooling. It seems that MiG and TiG welding processes centralize / localize the heat and the rest of the part is cooler so when the part cools it would crack about an 1/8" to a 1/4 " from the welded area. Now when brazing the pump to pick up the entire casting gets heated and after brazing cooled more uniformly and didn't develop any cracks. I'm sure there are some really good welders out there that can perform this process differently but I've never had a failure to this date.
Like my Dad used to say, there's more then one way to skin a cat !
Respectfully,
Henry Kunz 1534 H/SA